Pritidenta | priti®multidisc ZrO2, Multi Translucent
Translucency 49%
Bending strength >1,100 MPa
Suitable for
Аll open milling machines that accept round blanks with a diameter of 98.5 mm.
Description
Indications
You can use priti®multidisc ZrO2 multicolor Multi Translucent to fabricate partial crowns, monolithic, fully anatomical and partially or fully veneered crowns and bridges of up to 16 points and custom anterior and posterior supra structures on natural abutment teeth and implants.
The material combines very high flexural strength with good translucency. It is therefore particularly recommended as a scaffold material for esthetic veneering.
Is a flexible choice for solid and original work.
Material
- Zirconium dioxide Type II, Class 5 (DIN EN ISO 6872)
- Bending strength >1,100 MPa
- Translucency 49%
- High esthetics
- CTE (10,5 ± 0,5) ·10-6·K-1
- Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth
- Precise edges and margins due to highly compacted material
- Veneering is possible with any ceramic mapped to the CTE of ZrO2
- Cross-batch colour fidelity
- Homogeneous disc shading
- Colour can be reproduced at any time
- Biocompatible