Pritidenta | priti®multidisc ZrO2, Multicolor High Translucent
Translucency 49%
Bending strength >650 MPa
Suitable for
All open milling machines accept round blanks with a diameter of 98.5mm.
Description
The positioning and colour mapping can be adjusted to the right blank height depending on the restoration height.
| Restoration height | Blank height |
|---|---|
| 6 mm – 9 mm | 14 mm |
| 9 mm – 12 mm | 18 mm |
| 12 mm – 14 mm | 20 mm |
| 14 mm – 18 mm | 25 mm |
The positioning data apply mainly to anteriors. For posteriors, we recommend a lower position. This prevents fused cusp areas from appearing too white. An additional positive effect is the warm base hue due to the fissure pits.
Indications
You can use priti®multidisc ZrO2 multicolor High Translucent to fabricate inlays, onlays, veneers, partial crowns, anatomically reduced and monolithic, fully anatomical crowns and bridges of three pontics for anterior and posterior areas.
The translucency is comparable to that of lithium disilicate. Thanks to the high transparency and integrated colour gradient, the material is particularly recommended for the manufacture of unveneered restorations.
The esthetics
priti®multidisc ZrO2 multicolour High Translucent is the material of choice for the most vibrant and highest esthetics of restorations of three pontics.
Material
- Zirconium dioxide Type II, Class 4 (DIN EN ISO 6872)
- Bending strength >650 MPa
- High translucency 49%
- Brilliant esthetics
- CTE (10,5 ± 0,5) ·10-6·K-1
- Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth area
- Precise edges and margins due to highly compacted materials
- Veneering is possible with any ceramic mapped to the CTE of ZrO2
- Cross-batch colour fidelity
- Homogeneous disc shading
- Colour can be reproduced at any time
- Biocompatible