Pritidenta | priti®multidisc ZrO2, Monochrome Translucent
Translucency 40%
Bending strength >1,150 MPa
Description
Indications
Suitable for priti®multidisc ZrO2Translucent to fabricate partial crowns, monolithic, fully anatomical and partially or fully veneered crowns and bridges (up to 16 pontics) and custom anterior and posterior supra structures on natural abutment teeth and implants. The discs are available in white and pre-stained 16 VITA® shadesThe material combines very high flexural strength with good translucency. It is therefore particularly recommended as a scaffold material for esthetic veneering.
Material
- Zirconium dioxide Type II, Class 4 (DIN EN ISO 6872)
- Bending strength >1,150 MPa
- High translucency 40%
- Brilliant esthetics
- CTE (10,5 ± 0,5) ·10-6·K-1
- Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth
- Precise edges and margins due to highly compacted material
- Veneering is possible with any ceramic mapped to the CTE of ZrO2
- Cross-batch colour fidelity
- Homogeneous disc shading
- Colour can be reproduced at any time
- Biocompatible